近期,我院新能源本科生刘欣雨(共一)、孟希希(共一),教师王雨鑫(通讯)、张刘挺(通讯)等的研究成果“Polymeric carbon nitride supported single-phase Ni with exceptional catalytic effect on MgH2 for hydrogen storage”在《Journal of Alloys and Compounds》(IF=6.3)上发表。

发布时间:2025-07-04浏览次数:10

近期,我院新能源本科生刘欣雨(共一)、孟希希(共一),教师王雨鑫(通讯)、张刘挺(通讯)等的研究成果Polymeric carbon nitride supported single-phase Ni with exceptional catalytic effect on MgH2 for hydrogen storage在《Journal of Alloys and Compounds》(IF=6.3)上发表。


论文简介如下:

Magnesium hydride (MgH2) with its high hydrogen storage capacity (7.6 wt%) and exceptional reversibility, has emerged as a promising solid-state hydrogen storage material. This study designed a polymeric carbon nitride (PCN) supported single-phase Ni catalyst with superior thermal stability and catalytic activity. The optimized PCN-Ni catalyst significantly reduced the initial dehydrogenation temperature of MgH2 to 192 ºC. At 295 ºC, the composite released 6.10 wt% H2 within 5 min, and it subsequently absorbed 5.50 wt% H2 within 5 min at 150 ºC. Compared to pristine MgH2, the activation energies for dehydrogenation and hydrogen absorption were reduced by 31.6% and 29.4%, respectively. Moreover, the MgH2 + 10 wt% PCN-Ni composite exhibited remarkable cycling stability, with capacity retention rates of 96.0% and 96.7% after 20 hydrogenation/dehydrogenation cycles. In conclusion, this work provides a new perspective on the heterogeneous synergy of transition metal and carbon nitride composite catalysts in promoting the dehydrogenation/rehydrogenation reactions of MgH2 and lays the foundation for the design and fabrication of highly efficient catalysts in other energy storage related fields.